- 密度 [g/cm3]: 2.0
- 吸水率 [%]: 0.1
- 缺口沖擊強(qiáng)度: 0.473
- 彎曲強(qiáng)度 [MPa]: 64.0
- 彎曲模量 [MPa]: 15.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.00 g/cc | 0.0723 lb/in3 | ASTM D792A |
| Water Absorption | 0.10 % | 0.10 % | 24 hours R.T. ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | Positive Mold; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 64.0 MPa | 9280 psi | ASTM D651 |
| Flexural Strength | 88.0 MPa | 12800 psi | ASTM D790 |
| Flexural Modulus | 15.0 GPa | 2180 ksi | ASTM D790 |
| Compressive Strength | 176 MPa | 25500 psi | ASTM D695 |
| Izod Impact, Notched | 0.473 J/cm | 0.886 ft-lb/in | ASTM D256A |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 9.40 kV/mm | 239 kV/in | Short Time; Dry; ASTM D149 |
| Arc Resistance | 190 sec | 190 sec | ASTM D495 |
| Comparative Tracking Index | 175 - 250 V @Thickness 3.05 mm | 175 - 250 V @Thickness 0.120 in | UL PLC 3 (175-250 V) |
| Hot Wire Ignition, HWI | 60 - 120 sec @Thickness 3.05 mm | 60 - 120 sec @Thickness 0.120 in | UL PLC 1 |
| High Amp Arc Ignition, HAI | >= 120 arcs @Thickness 3.05 mm | >= 120 arcs @Thickness 0.120 in | UL PLC 0 |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 - 10.0 mm/min @Thickness 3.05 mm | 0.000 - 0.394 in/min @Thickness 0.120 in | UL PLC 0 (0-10 mm/min) |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 150 °C | 302 °F | UL RTI |
| Deflection Temperature at 1.8 MPa (264 psi) | 288 °C | 550 °F | ASTM D648 |
| UL RTI, Electrical | 150 °C | 302 °F | |
| UL RTI, Mechanical with Impact | 150 °C | 302 °F | |
| UL RTI, Mechanical without Impact | 150 °C | 302 °F | |
| Flammability, UL94 | V-0 | V-0 | |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 155 - 180 °C | 311 - 356 °F | |