- 密度 [g/cm3]: 1.37
- 吸水率 [%]: 0.8
- 缺口沖擊強度: 1.261
- 彎曲強度 [MPa]: 58.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in3 | ASTM D792A |
| Water Absorption | 0.80 % | 0.80 % | 24 hours R.T. ASTM D570 |
| Linear Mold Shrinkage | 0.0025 cm/cm | 0.0025 in/in | Positive Mold; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 76 | 76 | ASTM D785 |
| Hardness, Rockwell M | 108 | 108 | ASTM D785 |
| Tensile Strength, Ultimate | 58.0 MPa | 8410 psi | ASTM D651 |
| Flexural Strength | 83.0 MPa | 12000 psi | ASTM D790 |
| Compressive Strength | 169 MPa | 24500 psi | ASTM D695 |
| Izod Impact, Notched | 1.261 J/cm | 2.362 ft-lb/in | ASTM D256A |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 9.60 kV/mm | 244 kV/in | Short Time; Dry; ASTM D149 |
| Arc Resistance | 115 sec | 115 sec | ASTM D495 |
| Comparative Tracking Index | 175 - 250 V @Thickness 3.05 mm | 175 - 250 V @Thickness 0.120 in | UL PLC 4 (100-175 V) |
| Hot Wire Ignition, HWI | >= 0.00 sec @Thickness 3.05 mm | >= 0.00 sec @Thickness 0.120 in | UL PLC 0 |
| High Amp Arc Ignition, HAI | >= 120 arcs @Thickness 3.05 mm | >= 120 arcs @Thickness 0.120 in | UL PLC 0 |
| High Voltage Arc-Tracking Rate, HVTR | 81.0 - 150 mm/min @Thickness 3.05 mm | 3.19 - 5.91 in/min @Thickness 0.120 in | UL PLC 3 (81-150 mm/min) |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 40.0 μm/m-°C @Temperature 20.0 °C | 22.2 μin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Maximum Service Temperature, Air | 150 °C | 302 °F | UL RTI |
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | ASTM D648 |
| UL RTI, Electrical | 150 °C | 302 °F | |
| UL RTI, Mechanical with Impact | 150 °C | 302 °F | |
| UL RTI, Mechanical without Impact | 150 °C | 302 °F | |
| Flammability, UL94 | V-0 | V-0 | |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 150 - 175 °C | 302 - 347 °F | |