- 密度 [g/cm3]: 1.75
- 吸水率 [%]: 0.15
- 缺口沖擊強度: 0.473
- 彎曲強度 [MPa]: 65.0
- 彎曲模量 [MPa]: 17.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.75 g/cc | 0.0632 lb/in3 | ASTM D792A |
| Water Absorption | 0.15 % | 0.15 % | 24 hours R.T. ASTM D570 |
| Linear Mold Shrinkage | 0.0015 cm/cm | 0.0015 in/in | Positive Mold; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 100 | 100 | ASTM D785 |
| Hardness, Rockwell M | 120 | 120 | ASTM D785 |
| Tensile Strength, Ultimate | 65.0 MPa | 9430 psi | ASTM D651 |
| Flexural Strength | 166 MPa | 24100 psi | ASTM D790 |
| Flexural Modulus | 17.0 GPa | 2470 ksi | ASTM D790 |
| Compressive Strength | 276 MPa | 40000 psi | ASTM D695 |
| Izod Impact, Notched | 0.473 J/cm | 0.886 ft-lb/in | ASTM D256A |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.20e+11 ohm-cm | 1.20e+11 ohm-cm | ASTM D257 |
| Dielectric Strength | 14.6 kV/mm | 371 kV/in | Short Time; Dry; ASTM D149 |
| Arc Resistance | 180 sec | 180 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 38.0 μm/m-°C @Temperature 20.0 °C | 21.1 μin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 270 °C | 518 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 155 - 180 °C | 311 - 356 °F | |
- 關(guān)鍵詞:
- 供應
- Glass Reinforced
- 酚醛樹脂
- Resinoid 7051 SS Phenolic Molding