- 密度 [g/cm3]: 1.4
- 吸水率 [%]: 1.1
- 缺口沖擊強度: 0.683
- 彎曲強度 [MPa]: 41.0
- 彎曲模量 [MPa]: 11.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in3 | ASTM D792A |
| Water Absorption | 1.1 % | 1.1 % | 24 hours R.T. ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | Positive Mold; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 86 | 86 | ASTM D785 |
| Hardness, Rockwell M | 112 | 112 | ASTM D785 |
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D651 |
| Flexural Strength | 69.0 MPa | 10000 psi | ASTM D790 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| Compressive Strength | 145 MPa | 21000 psi | ASTM D695 |
| Izod Impact, Notched | 0.683 J/cm | 1.28 ft-lb/in | ASTM D256A |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 10.0 kV/mm | 254 kV/in | Short Time; Dry; ASTM D149 |
| Comparative Tracking Index | 175 - 250 V @Thickness 3.05 mm | 175 - 250 V @Thickness 0.120 in | UL PLC 4 (100-175 V) |
| Hot Wire Ignition, HWI | 60 - 120 sec @Thickness 3.05 mm | 60 - 120 sec @Thickness 0.120 in | UL PLC 1; UL PLC 1 |
| High Amp Arc Ignition, HAI | >= 120 arcs @Thickness 3.05 mm | >= 120 arcs @Thickness 0.120 in | UL PLC 0; UL PLC 0 |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min @Thickness 3.05 mm | >= 5.91 in/min @Thickness 0.120 in | UL PLC 4 (150+ mm/min) |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 150 °C | 302 °F | UL RTI |
| Deflection Temperature at 1.8 MPa (264 psi) | 121 °C | 250 °F | ASTM D648 |
| UL RTI, Electrical | 150 °C | 302 °F | |
| UL RTI, Mechanical with Impact | 150 °C | 302 °F | |
| UL RTI, Mechanical without Impact | 150 °C | 302 °F | |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 155 - 180 °C | 311 - 356 °F | |