- 密度 [g/cm3]: 1.75
- 吸水率 [%]: 0.1
- 缺口沖擊強度: 1.838
- 彎曲強度 [MPa]: 48.0
- 彎曲模量 [MPa]: 18.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.75 g/cc | 0.0632 lb/in3 | ASTM D792A |
| Water Absorption | 0.10 % | 0.10 % | 24 hours R.T. ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 48.0 MPa | 6960 psi | ASTM D651 |
| Flexural Strength | 138 MPa | 20000 psi | ASTM D790 |
| Flexural Modulus | 18.0 GPa | 2610 ksi | ASTM D790 |
| Compressive Strength | 240 MPa | 34800 psi | ASTM D695 |
| Izod Impact, Notched | 1.838 J/cm | 3.443 ft-lb/in | ASTM D256A |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 13.0 kV/mm | 330 kV/in | Short Time; Dry; ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 300 °C | >= 572 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 155 - 180 °C | 311 - 356 °F | |