- 拉伸強度 [MPa]: 103.0
- 彎曲模量 [MPa]: 22.8
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Volatiles | 1.0 - 3.0 % @Temperature 135 °C | 1.0 - 3.0 % @Temperature 275 °F | 8 min | ||
| Thickness | 559 microns | 22.0 mil | nominal, cured, per ply | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 103 MPa @Temperature 23.9 °C | 15000 psi @Temperature 75.0 °F | 0° Direction, Dry; ASTM D638 | ||
| Tensile Modulus | 17.2 GPa @Temperature 23.9 °C | 2500 ksi @Temperature 75.0 °F | 0° Direction, Dry; ASTM D638 | ||
| Flexural Strength | 186 MPa @Temperature 23.9 °C | 27000 psi @Temperature 75.0 °F | Dry; ASTM D790 | ||
| Flexural Modulus | 22.8 GPa @Temperature 23.9 °C | 3300 ksi @Temperature 75.0 °F | Dry; ASTM D790 | ||
| Compressive Strength | 448 MPa @Temperature 23.9 °C | 65000 psi @Temperature 75.0 °F | Dry; ASTM D695 | ||
| Compressive Modulus | 21.4 GPa @Temperature 23.9 °C | 3100 ksi @Temperature 75.0 °F | Dry; ASTM D695 | ||
| Processing Properties | Metric | English | Comments | ||
| Shelf Life | 6.00 Month @Temperature 4.44 °C | 6.00 Month @Temperature 40.0 °F | |||
| Descriptive Properties | |||||
| Resin Flow (%) | 1-5 | 260°F, 150psi | |||
| Resin Solids Content (%) | 27-30 | ||||