- 拉伸強度 [MPa]: 531.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Volatiles | <= 3.5 % @Temperature 135 °C | <= 3.5 % @Temperature 275 °F | 8 min | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 531 MPa @Temperature 23.9 °C | 77000 psi @Temperature 75.0 °F | 0° Direction, Dry; Press Cure, 16min, 300°F; ASTM D638 | ||
| Tensile Modulus | 57.2 GPa @Temperature 23.9 °C | 8300 ksi @Temperature 75.0 °F | 0° Direction, Dry; Press Cure, 16min, 300°F; ASTM D638 | ||
| Compressive Strength | 696 MPa @Temperature 23.9 °C | 101000 psi @Temperature 75.0 °F | Dry; Press Cure, 16min, 300°F; ASTM D695 | ||
| Compressive Modulus | 54.5 GPa @Temperature 23.9 °C | 7900 ksi @Temperature 75.0 °F | Dry; Press Cure, 16min, 300°F; ASTM D695 | ||
| Optical Properties | Metric | English | Comments | ||
| Optical Density | 1.0 | 1.0 | Dm, Flaming Mode; FAR 25.853, Part 25 Appendix F, Part V | ||
| Processing Properties | Metric | English | Comments | ||
| Gel Time | 7.00 min | 7.00 min | |||
| Shelf Life | 6.00 Month @Temperature 4.44 °C | 6.00 Month @Temperature 40.0 °F | |||
| Descriptive Properties | |||||
| Burn Length (in) | 1.8 | Vertical Burn, 60 sec; FAR 25.853, Part 25 Appendix F, Part I (b) (4) | |||
| Climbing Drum Peel (in-lb/3in) | 8 | ASTM D1781; Dry, 75°F; Press Cure, 16min, 300°F | |||
| Drip | None | Vertical Burn, 60 sec; FAR 25.853, Part 25 Appendix F, Part I (b) (4) | |||
| Fabric Area Weight (g/m2) | 193 | ||||
| Heat Release, Peak (KW/m2) | 32 | FAR 25.853 Part 25 Appendix F, Part IV | |||
| Heat Release, Total (KW-min/m2) | 19 | FAR 25.853 Part 25 Appendix F, Part IV | |||
| Prepreg Resin Content (%) | 38-44 | ||||
| Resin Flow (%) | 10-30 | 260°F, 150psi | |||
| Self Extinguish Time (sec) | 0 | Vertical Burn, 60 sec; FAR 25.853, Part 25 Appendix F, Part I (b) (4) | |||