- 拉伸強度 [MPa]: 352.0
- 彎曲模量 [MPa]: 23.4
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 2.08 g/cc | 2.08 g/cc | 18oz. woven roving form; ASTM D792 | ||
| Volatiles | 2.0 - 5.0 % @Temperature 163 °C | 2.0 - 5.0 % @Temperature 325 °F | 5 min | ||
| Thickness | 508 microns | 20.0 mil | per ply, 18oz. woven roving form | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Barcol | 68 | 68 | 18oz. woven roving form; ASTM D2583 | ||
| Tensile Strength, Yield | 352 MPa @Temperature 23.9 °C | 51000 psi @Temperature 75.0 °F | 0° Direction, Dry; 18oz. Woven roving form; ASTM D638 | ||
| Tensile Modulus | 29.0 GPa @Temperature 23.9 °C | 4200 ksi @Temperature 75.0 °F | 0° Direction, Dry; 18oz. Woven roving form; ASTM D638 | ||
| Flexural Strength | 229 MPa @Temperature 23.9 °C | 33200 psi @Temperature 75.0 °F | Dry; 18oz. Woven roving form; ASTM D790 | ||
| Flexural Modulus | 23.4 GPa @Temperature 23.9 °C | 3400 ksi @Temperature 75.0 °F | Dry; 18oz. Woven roving form; ASTM D790 | ||
| Compressive Strength | 152 MPa @Temperature 23.9 °C | 22000 psi @Temperature 75.0 °F | Dry; 18oz. Woven roving form; ASTM D695 | ||
| Compressive Modulus | 32.4 GPa @Temperature 23.9 °C | 4700 ksi @Temperature 75.0 °F | Dry; 18oz. Woven roving form; ASTM D695 | ||
| Processing Properties | Metric | English | Comments | ||
| Shelf Life | 6.00 Month @Temperature 4.44 °C | 6.00 Month @Temperature 40.0 °F | |||
| Descriptive Properties | |||||
| Fabric Area Weight (g/m2) | 610 | ||||
| Prepreg Resin Content (%) | 28-34 | ||||