- 拉伸強度 [MPa]: 48.3
- 彎曲模量 [MPa]: 15.9
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.37 g/cc | 1.37 g/cc | 8HS form; ASTM D792 | ||
| 1.47 g/cc | 1.47 g/cc | CMC form; ASTM D792 | |||
| Volatiles | 2.0 - 5.0 % @Temperature 163 °C | 2.0 - 5.0 % @Temperature 325 °F | 5 min | ||
| Thickness | 483 microns | 19.0 mil | per ply, 8HS form | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Barcol | 75 | 75 | 8HS form; ASTM D2583 | ||
| 81 | 81 | CMC form; ASTM D2583 | |||
| Tensile Strength, Yield | 48.3 MPa @Temperature 23.9 °C | 7000 psi @Temperature 75.0 °F | 0° Direction, Dry; CMC form; ASTM D638 | ||
| 241 MPa @Temperature 23.9 °C | 35000 psi @Temperature 75.0 °F | 0° Direction, Dry; 8HS form; ASTM D638 | |||
| Tensile Modulus | 15.9 GPa @Temperature 23.9 °C | 2300 ksi @Temperature 75.0 °F | 0° Direction, Dry; 8HS form; ASTM D638 | ||
| 17.2 GPa @Temperature 23.9 °C | 2500 ksi @Temperature 75.0 °F | 0° Direction, Dry; CMC form; ASTM D638 | |||
| Flexural Strength | 138 MPa @Temperature 23.9 °C | 20000 psi @Temperature 75.0 °F | Dry; CMC form; ASTM D790 | ||
| 448 MPa @Temperature 23.9 °C | 65000 psi @Temperature 75.0 °F | Dry; 8HS form; ASTM D790 | |||
| Flexural Modulus | 15.9 GPa @Temperature 23.9 °C | 2300 ksi @Temperature 75.0 °F | Dry; 8HS form; ASTM D790 | ||
| 17.2 GPa @Temperature 23.9 °C | 2500 ksi @Temperature 75.0 °F | Dry; CMC form; ASTM D790 | |||
| Compressive Strength | 290 MPa @Temperature 23.9 °C | 42000 psi @Temperature 75.0 °F | Dry; CMC form; ASTM D695 | ||
| 317 MPa @Temperature 23.9 °C | 46000 psi @Temperature 75.0 °F | Dry; 8HS form; ASTM D695 | |||
| Compressive Modulus | 16.5 GPa @Temperature 23.9 °C | 2400 ksi @Temperature 75.0 °F | Dry; CMC form; ASTM D695 | ||
| 22.1 GPa @Temperature 23.9 °C | 3200 ksi @Temperature 75.0 °F | Dry; 8HS form; ASTM D695 | |||
| Shear Strength | 30.3 MPa @Temperature 23.9 °C | 4400 psi @Temperature 75.0 °F | Short Beam; Dry; 8HS form; ASTM D5379 | ||
| 30.3 MPa @Temperature 23.9 °C | 4400 psi @Temperature 75.0 °F | Short Beam; Dry; CMC form; ASTM D5379 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 15.5 μm/m-°C @Temperature 204 °C | 8.60 μin/in-°F @Temperature 400 °F | with ply; 8HS form; ASTM D696 | ||
| Processing Properties | Metric | English | Comments | ||
| Shelf Life | 6.00 Month @Temperature 4.44 °C | 6.00 Month @Temperature 40.0 °F | |||
| Descriptive Properties | |||||
| Fabric Area Weight (g/m2) | 330 | ||||
| Filler Content (%) | 9-15 | ||||
| Prepreg Resin Content (%) | 31-37 | ||||
| Resin Flow (%) | 5-20 | 325°F, 150psi | |||