- 密度 [g/cm3]: 1.46
- 吸水率 [%]: 0.4
- 缺口沖擊強度: 0.29
- 斷裂伸長率 [%]: 83.0
- 彎曲強度 [MPa]: 52.0
- 彎曲模量 [MPa]: 6.90
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in3 | ASTM D792 |
| Apparent Bulk Density | 0.500 g/cc | 0.0181 lb/in3 | ASTM D1895 |
| Water Absorption | 0.40 % | 0.40 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0045 cm/cm | 0.0045 in/in | Compression; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
| Flexural Yield Strength | 83.0 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 6.90 GPa | 1000 ksi | ASTM D790 |
| Compressive Yield Strength | 166 MPa | 24100 psi | ASTM D695 |
| Izod Impact, Notched | 0.290 J/cm | 0.543 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 2.20e+10 ohm-cm | 2.20e+10 ohm-cm | ASTM D257 |
| Dielectric Strength | 12.2 kV/mm | 310 kV/in | ASTM D149 |
| Comparative Tracking Index | 180 V | 180 V | UL 746 |
| Thermal Properties | Metric | English | Comments |
| UL RTI, Electrical | 150 °C @Thickness 1.60 mm | 302 °F @Thickness 0.0630 in | |
| UL RTI, Mechanical with Impact | 150 °C @Thickness 1.60 mm | 302 °F @Thickness 0.0630 in | |
| UL RTI, Mechanical without Impact | 150 °C @Thickness 1.60 mm | 302 °F @Thickness 0.0630 in | |
| Flammability, UL94 | V-0 @Thickness 6.10 mm | V-0 @Thickness 0.240 in | |
| V-0 @Thickness 6.10 mm | V-0 @Thickness 0.240 in | ||