- 拉伸強度 [MPa]: 414.0
- 彎曲模量 [MPa]: 24.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.70 g/cc | 1.70 g/cc | ASTM D792 | ||
| Volatiles | 2.0 - 5.0 % @Temperature 135 °C | 2.0 - 5.0 % @Temperature 275 °F | 8 min | ||
| Thickness | 305 microns | 12.0 mil | cured laminate, per ply | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Barcol | 75 | 75 | ASTM D2583 | ||
| Tensile Strength, Yield | 414 MPa @Temperature 23.9 °C | 60000 psi @Temperature 75.0 °F | 0° Direction, Dry; 325°F Autoclave Cured; ASTM D638 | ||
| Tensile Modulus | 24.1 GPa @Temperature 23.9 °C | 3500 ksi @Temperature 75.0 °F | 0° Direction, Dry; 325°F Autoclave Cured; ASTM D638 | ||
| Flexural Strength | 586 MPa @Temperature 23.9 °C | 85000 psi @Temperature 75.0 °F | Dry; 325°F Autoclave Cured; ASTM D790 | ||
| Flexural Modulus | 24.1 GPa @Temperature 23.9 °C | 3500 ksi @Temperature 75.0 °F | Dry; 325°F Autoclave Cured; ASTM D790 | ||
| Compressive Strength | 448 MPa @Temperature 23.9 °C | 65000 psi @Temperature 75.0 °F | Dry; 325°F Autoclave Cured; ASTM D695 | ||
| Compressive Modulus | 24.8 GPa @Temperature 23.9 °C | 3600 ksi @Temperature 75.0 °F | Dry; 325°F Autoclave Cured; ASTM D695 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 8.10 μm/m-°C @Temperature 26.7 - 204 °C | 4.50 μin/in-°F @Temperature 80.0 - 400 °F | with ply; ASTM D696 | ||
| 34.2 μm/m-°C @Temperature 26.7 - 204 °C | 19.0 μin/in-°F @Temperature 80.0 - 400 °F | x-ply; ASTM D696 | |||
| Specific Heat Capacity | 0.837 J/g-°C @Temperature 23.9 °C | 0.200 BTU/lb-°F @Temperature 75.0 °F | ASTM C351 | ||
| Processing Properties | Metric | English | Comments | ||
| Gel Time | 0.800 - 3.30 min | 0.800 - 3.30 min | |||
| Shelf Life | 3.00 Month @Temperature 4.44 °C | 3.00 Month @Temperature 40.0 °F | |||
| 6.00 Month @Temperature -17.8 °C | 6.00 Month @Temperature 0.000 °F | ||||
| Descriptive Properties | |||||
| Fabric Area Weight (g/m2) | 475 | ||||
| Prepreg Resin Content (%) | 33-39 | ||||
| Resin Flow (%) | 5-20 | 325°F, 15psi | |||