- 密度 [g/cm3]: 1.85
- 吸水率 [%]: 0.1
- 缺口沖擊強度: 0.578
- 彎曲強度 [MPa]: 52.0
- 彎曲模量 [MPa]: 16.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.85 g/cc | 0.0668 lb/in3 | ASTM D792A |
| Water Absorption | 0.10 % | 0.10 % | 24 hours R.T. ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D651 |
| Flexural Strength | 90.0 MPa | 13100 psi | ASTM D790 |
| Flexural Modulus | 16.0 GPa | 2320 ksi | ASTM D790 |
| Compressive Strength | 200 MPa | 29000 psi | ASTM D695 |
| Izod Impact, Notched | 0.578 J/cm | 1.08 ft-lb/in | ASTM D256A |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 9.40 kV/mm | 239 kV/in | Short Time; Dry; ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 300 °C | >= 572 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 155 - 180 °C | 311 - 356 °F | |