- 密度 [g/cm3]: 1.9
- 吸水率 [%]: 0.1
- 缺口沖擊強度: 0.446
- 彎曲強度 [MPa]: 48.0
- 彎曲模量 [MPa]: 14.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.90 g/cc | 0.0686 lb/in3 | ASTM D792A |
| Water Absorption | 0.10 % | 0.10 % | 24 hours R.T. ASTM D570 |
| Linear Mold Shrinkage | 0.0035 cm/cm | 0.0035 in/in | Positive Mold; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 48.0 MPa | 6960 psi | ASTM D651 |
| Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
| Flexural Modulus | 14.0 GPa | 2030 ksi | ASTM D790 |
| Compressive Strength | 170 MPa | 24700 psi | ASTM D695 |
| Izod Impact, Notched | 0.446 J/cm | 0.836 ft-lb/in | ASTM D256A |
| Electrical Properties | Metric | English | Comments |
| Comparative Tracking Index | 250 - 399 V @Thickness 3.05 mm | 250 - 399 V @Thickness 0.120 in | UL PLC 2 (250-399 V) |
| Hot Wire Ignition, HWI | >= 120 sec @Thickness 3.05 mm | >= 120 sec @Thickness 0.120 in | UL PLC 0; UL PLC 0 |
| High Amp Arc Ignition, HAI | >= 120 arcs @Thickness 3.05 mm | >= 120 arcs @Thickness 0.120 in | UL PLC 0; UL PLC 0 |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 - 10.0 mm/min @Thickness 3.05 mm | 0.000 - 0.394 in/min @Thickness 0.120 in | UL PLC 0 (0-10 mm/min) |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 150 °C | 302 °F | |
| UL RTI, Electrical | 150 °C | 302 °F | |
| UL RTI, Mechanical with Impact | 150 °C | 302 °F | |
| UL RTI, Mechanical without Impact | 150 °C | 302 °F | |
| Flammability, UL94 | V-0 | V-0 | |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 155 - 180 °C | 311 - 356 °F | |