- 密度 [g/cm3]: 1.6
- 吸水率 [%]: 0.2
- 缺口沖擊強度: 0.341
- 彎曲模量 [MPa]: 8.90
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in3 | ASTM D792A |
| Water Absorption | 0.20 % | 0.20 % | 24 hours R.T. ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | Positive Mold; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Flexural Strength | 85.0 MPa | 12300 psi | ASTM D790 |
| Flexural Modulus | 8.90 GPa | 1290 ksi | ASTM D790 |
| Compressive Strength | 110 MPa | 16000 psi | ASTM D695 |
| Izod Impact, Notched | 0.341 J/cm | 0.639 ft-lb/in | ASTM D256A |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 12.8 kV/mm | 325 kV/in | Short Time; Dry; ASTM D149 |
| Arc Resistance | 130 sec | 130 sec | ASTM D495 |
| Comparative Tracking Index | 175 - 250 V @Thickness 3.05 mm | 175 - 250 V @Thickness 0.120 in | UL PLC 3 (175-250 V) |
| Hot Wire Ignition, HWI | >= 0.00 sec @Thickness 3.05 mm | >= 0.00 sec @Thickness 0.120 in | UL PLC 0 |
| High Amp Arc Ignition, HAI | 15 - 29 arcs @Thickness 6.10 mm | 15 - 29 arcs @Thickness 0.240 in | UL PLC 3, 15-29 arcs |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 - 10.0 mm/min @Thickness 6.10 mm | 0.000 - 0.394 in/min @Thickness 0.240 in | UL PLC 0 (0-10 mm/min) |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 150 °C | 302 °F | UL RTI |
| Deflection Temperature at 1.8 MPa (264 psi) | 275 °C | 527 °F | ASTM D648 |
| UL RTI, Electrical | 150 °C | 302 °F | |
| UL RTI, Mechanical with Impact | 150 °C | 302 °F | |
| UL RTI, Mechanical without Impact | 150 °C | 302 °F | |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 155 - 180 °C | 311 - 356 °F | |