- 密度 [g/cm3]: 1.7
- 吸水率 [%]: 0.1
- 缺口沖擊強度: 0.16
- 斷裂伸長率 [%]: 83.0
- 彎曲強度 [MPa]: 41.0
- 彎曲模量 [MPa]: 11.7
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.70 - 2.00 g/cc | 0.0614 - 0.0723 lb/in3 | Average value: 1.86 g/cc Grade Count:14 |
| Apparent Bulk Density | 0.740 - 0.800 g/cc | 0.0267 - 0.0289 lb/in3 | Average value: 0.770 g/cc Grade Count:4 |
| Water Absorption | 0.100 - 0.250 % | 0.100 - 0.250 % | Average value: 0.197 % Grade Count:6 |
| 0.110 - 0.300 % @Time 173000 - 173000 sec | 0.110 - 0.300 % @Time 48.0 - 48.0 hour | Average value: 0.202 % Grade Count:5 | |
| 0.110 - 0.300 % @Temperature 50.0 - 50.0 °C | 0.110 - 0.300 % @Temperature 122 - 122 °F | Average value: 0.202 % Grade Count:5 | |
| Linear Mold Shrinkage | 0.00100 - 0.00700 cm/cm | 0.00100 - 0.00700 in/in | Average value: 0.00367 cm/cm Grade Count:12 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Barcol | 60.0 - 70.0 | 60.0 - 70.0 | Average value: 65.9 Grade Count:7 |
| Tensile Strength, Ultimate | 41.0 - 107 MPa | 5950 - 15500 psi | Average value: 77.7 MPa Grade Count:13 |
| Flexural Yield Strength | 83.0 - 150 MPa | 12000 - 21800 psi | Average value: 117 MPa Grade Count:13 |
| Flexural Modulus | 11.7 - 19.0 GPa | 1700 - 2760 ksi | Average value: 14.6 GPa Grade Count:12 |
| Compressive Yield Strength | 172 - 379 MPa | 25000 - 55000 psi | Average value: 234 MPa Grade Count:13 |
| Izod Impact, Notched | 0.160 - 0.370 J/cm | 0.300 - 0.693 ft-lb/in | Average value: 0.282 J/cm Grade Count:12 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | Average value: 1.00e+15 ohm-cm Grade Count:4 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | Average value: 1.00e+15 ohm Grade Count:4 |
| Dielectric Constant | 3.00 - 4.80 | 3.00 - 4.80 | Average value: 4.03 Grade Count:13 |
| Dielectric Strength | 12.8 - 17.0 kV/mm | 325 - 432 kV/in | Average value: 14.0 kV/mm Grade Count:13 |
| Dissipation Factor | 0.00400 - 0.0200 | 0.00400 - 0.0200 | Average value: 0.0131 Grade Count:13 |
| Arc Resistance | 178 - 190 sec | 178 - 190 sec | Average value: 181 sec Grade Count:12 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 12.6 - 32.0 μm/m-°C | 7.00 - 17.8 μin/in-°F | Average value: 22.6 μm/m-°C Grade Count:12 |
| CTE, linear, Transverse to Flow | 26.4 - 80.0 μm/m-°C | 14.7 - 44.4 μin/in-°F | Average value: 58.5 μm/m-°C Grade Count:7 |
| Thermal Conductivity | 0.259 - 1.26 W/m-K | 1.80 - 8.72 BTU-in/hr-ft2-°F | Average value: 0.795 W/m-K Grade Count:7 |
| Deflection Temperature at 1.8 MPa (264 psi) | 165 - 282 °C | 329 - 540 °F | Average value: 229 °C Grade Count:10 |
| Glass Transition Temp, Tg | 110 - 165 °C | 230 - 329 °F | Average value: 151 °C Grade Count:5 |
| Flammability, UL94 | V-0 | V-0 | Grade Count:4 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 150 - 193 °C | 302 - 379 °F | Average value: 166 °C Grade Count:5 |