- 密度 [g/cm3]: 1.8
- 吸水率 [%]: 0.15
- 缺口沖擊強度: 0.31
- 彎曲模量 [MPa]: 19.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.800 g/cc | 0.0289 lb/in3 | ASTM D1895 | ||
| Density | 1.80 g/cc | 0.0650 lb/in3 | ASTM D792 | ||
| Water Absorption | 0.15 % @Temperature 50.0 °C, Time 173000 sec | 0.15 % @Temperature 122 °F, Time 48.0 hour | ASTM D570 | ||
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 71.0 MPa | 10300 psi | ASTM D638 | ||
| Flexural Strength | 145 MPa | 21000 psi | at rupture; ASTM D790 | ||
| Flexural Modulus | 19.0 GPa | 2760 ksi | ASTM D790 | ||
| Compressive Strength | 240 MPa | 34800 psi | ASTM D695 | ||
| Izod Impact, Notched | 0.310 J/cm | 0.581 ft-lb/in | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 4.0 @Frequency 1.00e+6 Hz | 4.0 @Frequency 1.00e+6 Hz | wet; ASTM D150 | ||
| Dielectric Strength | 13.2 kV/mm @Frequency 60.0 Hz | 335 kV/in @Frequency 60.0 Hz | step-by-step, wet; ASTM D149 | ||
| 15.3 kV/mm @Frequency 60.0 Hz | 389 kV/in @Frequency 60.0 Hz | short time, wet; ASTM D149 | |||
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | wet; ASTM D150 | ||
| Arc Resistance | 180 sec | 180 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 27.0 μm/m-°C | 15.0 μin/in-°F | ASTM E831 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | As Molded; ASTM D648A | ||
| >= 280 °C | >= 536 °F | Post Baked; ASTM D648A | |||
| Descriptive Properties | |||||
| Color | Black | ||||
| Form | Granular | ||||
| Molding Method | Compression | ||||
| Transfer | |||||