- 密度 [g/cm3]: 1.98
- 吸水率 [%]: 0.15
- 缺口沖擊強度: 0.26
- 彎曲模量 [MPa]: 15.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.900 g/cc | 0.0325 lb/in3 | ASTM D1895 | ||
| Density | 1.98 g/cc | 0.0715 lb/in3 | ASTM D792 | ||
| Water Absorption | 0.15 % @Temperature 50.0 °C, Time 173000 sec | 0.15 % @Temperature 122 °F, Time 48.0 hour | ASTM D570 | ||
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Barcol | 72 | 72 | ASTM D2583 | ||
| Tensile Strength at Break | 62.0 MPa | 8990 psi | ASTM D638 | ||
| Flexural Strength | 130 MPa | 18900 psi | at rupture; ASTM D790 | ||
| Flexural Modulus | 15.0 GPa | 2180 ksi | ASTM D790 | ||
| Compressive Strength | 190 MPa | 27600 psi | ASTM D695 | ||
| Izod Impact, Notched | 0.260 J/cm | 0.487 ft-lb/in | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 4.5 @Frequency 1.00e+6 Hz | 4.5 @Frequency 1.00e+6 Hz | wet; ASTM D150 | ||
| Dielectric Strength | 12.8 kV/mm @Frequency 60.0 Hz | 325 kV/in @Frequency 60.0 Hz | step-by-step, wet; ASTM D149 | ||
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | wet; ASTM D150 | ||
| Arc Resistance | 185 sec | 185 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 27.0 μm/m-°C | 15.0 μin/in-°F | ASTM E831 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 282 °C | >= 540 °F | Post Baked; ASTM D648A | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| Form | Granular | ||||
| Molding Method | Compression | ||||
| Injection | |||||
| Transfer | |||||