- 密度 [g/cm3]: 0.8
- 吸水率 [%]: 0.0034
- 缺口沖擊強度: 0.187
- 拉伸強度 [MPa]: 0.689
- 斷裂伸長率 [%]: 62.1
- 彎曲強度 [MPa]: 2.76
- 彎曲模量 [MPa]: 7.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.800 - 2.45 g/cc | 0.0289 - 0.0885 lb/in3 | Average value: 1.30 g/cc Grade Count:101 |
| Solids Content | 47.4 - 100 % | 47.4 - 100 % | Average value: 85.3 % Grade Count:6 |
| Water Absorption | 0.00340 - 0.900 % | 0.00340 - 0.900 % | Average value: 0.364 % Grade Count:33 |
| 0.250 - 0.600 % @Temperature 50.0 - 100 °C | 0.250 - 0.600 % @Temperature 122 - 212 °F | Average value: 0.425 % Grade Count:2 | |
| 0.250 - 0.600 % @Time 86400 - 173000 sec | 0.250 - 0.600 % @Time 24.0 - 48.0 hour | Average value: 0.425 % Grade Count:2 | |
| Loss On Ignition | 0.280 - 0.500 % @Temperature 150 - 155 °C | 0.280 - 0.500 % @Temperature 302 - 311 °F | Average value: 0.427 % Grade Count:3 |
| 0.280 - 0.500 % @Time 605000 - 605000 sec | 0.280 - 0.500 % @Time 168 - 168 hour | Average value: 0.427 % Grade Count:3 | |
| Moisture Vapor Transmission | <= 22.6771 cc-mm/m2-24hr-atm @Temperature 40.0 - 40.0 °C | <= 57.5999 cc-mil/100 in2-24hr-atm @Temperature 104 - 104 °F | Average value: 22.7 cc-mm/m2-24hr-atm Grade Count:1 |
| Viscosity | 1.00 - 1.10e+6 cP | 1.00 - 1.10e+6 cP | Average value: 25300 cP Grade Count:230 |
| 170 - 110000 cP @Temperature 40.0 - 175 °C | 170 - 110000 cP @Temperature 104 - 347 °F | Average value: 13800 cP Grade Count:12 | |
| Linear Mold Shrinkage | 0.00250 - 0.00700 cm/cm | 0.00250 - 0.00700 in/in | Average value: 0.00363 cm/cm Grade Count:7 |
| Spiral Flow | 63.0 - 130 cm | 24.8 - 51.2 in | Average value: 88.0 cm Grade Count:7 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 15.0 - 90.0 | 15.0 - 90.0 | Average value: 54.0 Grade Count:16 |
| Hardness, Shore D | 30.0 - 98.0 | 30.0 - 98.0 | Average value: 78.9 Grade Count:154 |
| 20.0 - 20.0 @Temperature 100 - 100 °C | 20.0 - 20.0 @Temperature 212 - 212 °F | Average value: 20.0 Grade Count:1 | |
| Tensile Strength, Ultimate | 2.76 - 552 MPa | 400 - 80000 psi | Average value: 45.4 MPa Grade Count:74 |
| >= 13.7895 MPa @Temperature 60.0 - 149 °C | >= 2000.00 psi @Temperature 140 - 300 °F | Average value: 24.1 MPa Grade Count:2 | |
| Tensile Strength, Yield | 0.689 - 85.1 MPa | 100 - 12300 psi | Average value: 22.8 MPa Grade Count:28 |
| Elongation at Break | 0.000 - 200 % | 0.000 - 200 % | Average value: 32.7 % Grade Count:38 |
| >= 30.0 % @Temperature 60.0 - 60.0 °C | >= 30.0 % @Temperature 140 - 140 °F | Average value: 30.0 % Grade Count:1 | |
| Elongation at Yield | 1.00 - 140 % | 1.00 - 140 % | Average value: 19.6 % Grade Count:7 |
| Modulus of Elasticity | 0.0138 - 6.00 GPa | 2.00 - 870 ksi | Average value: 2.35 GPa Grade Count:64 |
| 0.827371 - 1.86158 GPa @Temperature 60.0 - 149 °C | 120.002 - 270.004 ksi @Temperature 140 - 300 °F | Average value: 1.59 GPa Grade Count:3 | |
| Flexural Yield Strength | 62.1 - 137 MPa | 9000 - 19800 psi | Average value: 111 MPa Grade Count:12 |
| Flexural Modulus | 7.00 - 18.0 GPa | 1020 - 2610 ksi | Average value: 14.3 GPa Grade Count:8 |
| Compressive Yield Strength | 4.83 - 1930 MPa | 700 - 280000 psi | Average value: 123 MPa Grade Count:36 |
| Compressive Modulus | 0.0345 - 2.90 GPa | 5.00 - 420 ksi | Average value: 1.57 GPa Grade Count:23 |
| Shear Strength | 5.52 - 65.0 MPa | 800 - 9430 psi | Average value: 17.7 MPa Grade Count:32 |
| 15.8579 - 15.8579 MPa @Temperature 204 - 204 °C | 2300.00 - 2300.00 psi @Temperature 400 - 400 °F | Average value: 15.9 MPa Grade Count:2 | |
| Adhesive Bond Strength | 3.10 - 44.8 MPa | 450 - 6500 psi | Average value: 13.0 MPa Grade Count:32 |
| 7.58423 - 16.8922 MPa @Temperature -54.4 - 82.2 °C | 1100.00 - 2450.00 psi @Temperature -66.0 - 180 °F | Average value: 13.5 MPa Grade Count:3 | |
| Izod Impact, Notched | 0.187 - 0.694 J/cm | 0.350 - 1.30 ft-lb/in | Average value: 0.388 J/cm Grade Count:4 |
| Peel Strength | 0.351 - 7.89 kN/m | 2.00 - 45.0 pli | Average value: 3.49 kN/m Grade Count:13 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 5.00 - 3.00e+17 ohm-cm | 5.00 - 3.00e+17 ohm-cm | Average value: 4.97e+15 ohm-cm Grade Count:117 |
| 1.00e+8 - 5.80e+15 ohm-cm @Temperature 30.0 - 400 °C | 1.00e+8 - 5.80e+15 ohm-cm @Temperature 86.0 - 752 °F | Average value: 1.21e+15 ohm-cm Grade Count:7 | |
| Surface Resistance | 3.90e+14 - 3.90e+14 ohm @Temperature 149 - 149 °C | 3.90e+14 - 3.90e+14 ohm @Temperature 300 - 300 °F | Average value: 3.90e+14 ohm Grade Count:1 |
| Dielectric Constant | 2.70 - 6.30 | 2.70 - 6.30 | Average value: 4.01 Grade Count:147 |
| 2.94 - 4.70 @Temperature 30.0 - 204 °C | 2.94 - 4.70 @Temperature 86.0 - 399 °F | Average value: 3.60 Grade Count:7 | |
| 2.94 - 4.70 @Frequency 60.0 - 1.00e+6 Hz | 2.94 - 4.70 @Frequency 60.0 - 1.00e+6 Hz | Average value: 3.60 Grade Count:7 | |
| Dielectric Strength | 11.8 - 48.2 kV/mm | 300 - 1220 kV/in | Average value: 17.0 kV/mm Grade Count:103 |
| Dissipation Factor | 0.00100 - 0.120 | 0.00100 - 0.120 | Average value: 0.0154 Grade Count:58 |
| 0.00300 - 0.0700 @Temperature 30.0 - 204 °C | 0.00300 - 0.0700 @Temperature 86.0 - 399 °F | Average value: 0.0139 Grade Count:6 | |
| 0.00300 - 0.0700 @Frequency 60.0 - 1.00e+6 Hz | 0.00300 - 0.0700 @Frequency 60.0 - 1.00e+6 Hz | Average value: 0.0139 Grade Count:6 | |
| Arc Resistance | 120 - 200 sec | 120 - 200 sec | Average value: 175 sec Grade Count:8 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 4.00 - 275 μm/m-°C | 2.22 - 153 μin/in-°F | Average value: 63.3 μm/m-°C Grade Count:111 |
| 75.0 - 180 μm/m-°C @Temperature 60.0 - 60.0 °C | 41.7 - 100 μin/in-°F @Temperature 140 - 140 °F | Average value: 159 μm/m-°C Grade Count:5 | |
| CTE, linear, Transverse to Flow | 45.0 - 70.0 μm/m-°C | 25.0 - 38.9 μin/in-°F | Average value: 59.8 μm/m-°C Grade Count:7 |
| Thermal Conductivity | 0.140 - 3.46 W/m-K | 0.972 - 24.0 BTU-in/hr-ft2-°F | Average value: 0.729 W/m-K Grade Count:75 |
| Maximum Service Temperature, Air | 32.2 - 343 °C | 90.0 - 650 °F | Average value: 144 °C Grade Count:177 |
| Minimum Service Temperature, Air | -269 - 15.6 °C | -452 - 60.0 °F | Average value: -62.8 °C Grade Count:116 |
| Glass Transition Temp, Tg | -120 - 225 °C | -184 - 437 °F | Average value: 97.3 °C Grade Count:83 |
| Flammability, UL94 | V-0 | V-0 | Grade Count:8 |
| Flash Point | 100 - 200 °C | 212 - 392 °F | Average value: 164 °C Grade Count:8 |
| Shrinkage | 0.150 - 2.00 % | 0.150 - 2.00 % | Average value: 1.23 % Grade Count:3 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.48 - 1.57 | 1.48 - 1.57 | Average value: 1.54 Grade Count:5 |
| Transmission, Visible | 0.000 - 90.0 % | 0.000 - 90.0 % | Average value: 84.7 % Grade Count:17 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 22.2 - 185 °C | 72.0 - 365 °F | Average value: 129 °C Grade Count:14 |
| Cure Time | 3.00 - 18000 min | 0.0500 - 300 hour | Average value: 1260 min Grade Count:103 |
| 1.80 - 14400 min @Temperature 54.4 - 204 °C | 0.0300 - 240 hour @Temperature 130 - 400 °F | Average value: 310 min Grade Count:54 | |
| Pot Life | 2.00 - 40300 min | 2.00 - 40300 min | Average value: 1380 min Grade Count:112 |
| Gel Time | 90.0 - 720 min | 90.0 - 720 min | Average value: 300 min Grade Count:3 |
| 3.00 - 30.0 min @Temperature 65.0 - 150 °C | 3.00 - 30.0 min @Temperature 149 - 302 °F | Average value: 5.68 min Grade Count:12 | |
| Shelf Life | 3.00 - 12.0 Month | 3.00 - 12.0 Month | Average value: 8.77 Month Grade Count:52 |
| 3.00 - 6.00 Month @Temperature -40.0 - 60.0 °C | 3.00 - 6.00 Month @Temperature -40.0 - 140 °F | Average value: 5.80 Month Grade Count:15 | |
| Component Elements Properties | Metric | English | Comments |
| Potassium, K | 0.000100 - 0.000400 % | 0.000100 - 0.000400 % | Average value: 0.000137 % Grade Count:8 |
| Sodium, Na | 0.000100 - 0.000500 % | 0.000100 - 0.000500 % | Average value: 0.000450 % Grade Count:8 |