- 密度 [g/cm3]: 1.77
- 彎曲模量 [MPa]: 14.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.77 g/cc | 0.0639 lb/in3 | ISO 1183 | ||
| Filler Content | 40 % | 40 % | |||
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 2.00 mm | 0.0020 in/in @Thickness 0.0787 in | Parallel; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Thickness 2.00 mm | 0.0070 in/in @Thickness 0.0787 in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527 | ||
| Elongation at Break | 1.5 % | 1.5 % | ISO 527 | ||
| Tensile Modulus | 16.5 GPa | 2390 ksi | ISO 527 | ||
| Flexural Strength | 170 MPa @Temperature 23.0 °C | 24700 psi @Temperature 73.4 °F | ISO 178 | ||
| Flexural Modulus | 14.0 GPa @Temperature 23.0 °C | 2030 ksi @Temperature 73.4 °F | ISO 178 | ||
| Charpy Impact, Notched | 1.00 J/cm2 @Temperature 23.0 °C | 4.76 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 352 °C | 666 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 298 °C | 568 °F | ISO 75-1/-2 1993/N2 | ||
| Flammability, UL94 | V-0 @Thickness 0.750 mm | V-0 @Thickness 0.0295 in | IEC 60695-11-10 | ||
| V-0 @Thickness 0.400 mm | V-0 @Thickness 0.0157 in | IEC 60695-11-10 | |||
| V-0 @Thickness 0.750 mm | V-0 @Thickness 0.0295 in | UL94 | |||
| V-0 @Thickness 0.400 mm | V-0 @Thickness 0.0157 in | UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 365 °C | 689 °F | Optimum | ||
| 360 - 370 °C | 680 - 698 °F | ||||
| Mold Temperature | 80.0 °C | 176 °F | Optimum | ||
| 40.0 - 150 °C | 104 - 302 °F | ||||
| Drying Temperature | 150 °C | 302 °F | |||
| Dry Time | 3 hour | 3 hour | Dehumidified Dryer | ||
| Moisture Content | <= 0.010 % | <= 0.010 % | |||
| Descriptive Properties | |||||
| Color | Black | ||||
| Drying Recommended | Yes | ||||
| Filler | Glass Reinforced | ||||
| Forms | Pellets | ||||
| Generic | LCP | ||||
| Part Marking Code | >LCP-GF40< | ISO 11469 | |||
| Polymer Family | LCP | ||||
| Polymer Type | LCP | ||||
| Processing Method | Injection Molding | ||||
| Product Category | Glass Reinforced Resins | ||||
| Region Available | Americas | ||||
| Asia/Pacific | |||||
| Europe | |||||
| Resin Identification | LCP-GF40 | ISO 1043 | |||