- 密度 [g/cm3]: 1.67
- 彎曲模量 [MPa]: 6.60
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in3 | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527 | ||
| Elongation at Break | 3.8 % | 3.8 % | ISO 527 | ||
| Tensile Modulus | 8.50 GPa | 1230 ksi | ISO 527 | ||
| Flexural Strength | 135 MPa | 19600 psi | ISO 178 | ||
| Flexural Modulus | 6.60 GPa @Temperature 23.0 °C | 957 ksi @Temperature 73.4 °F | ISO 178 | ||
| Charpy Impact, Notched | 0.900 J/cm2 @Temperature 23.0 °C | 4.28 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 335 °C | 635 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO 75-1/-2 | ||
| UL RTI, Electrical | 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | UL 746B | ||
| UL RTI, Mechanical with Impact | 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | UL 746B | ||
| UL RTI, Mechanical without Impact | 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | UL 746B | ||
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | IEC 60695-11-10 | ||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 355 °C | 671 °F | Optimum | ||
| 350 - 360 °C | 662 - 680 °F | ||||
| Mold Temperature | 80.0 °C | 176 °F | Optimum | ||
| 40.0 - 150 °C | 104 - 302 °F | ||||
| Drying Temperature | 150 °C | 302 °F | |||
| Dry Time | 3 hour | 3 hour | Dehumidified Dryer | ||
| Moisture Content | <= 0.010 % | <= 0.010 % | |||
| Descriptive Properties | |||||
| Color | Black | ||||
| Drying Recommended | Yes | ||||
| Forms | Pellets | ||||
| Generic | LCP | ||||
| Part Marking Code | >LCP-(MD30+S)< | ISO 11469 | |||
| Polymer Family | LCP | ||||
| Polymer Type | LCP | ||||
| Processing Method | Injection Molding | ||||
| Product Category | Electrical Resins | ||||
| Flame Retardant Resins | |||||
| Low Warp Resins | |||||
| Mineral Reinforced Resins | |||||
| Region Available | Americas | ||||
| Asia/Pacific | |||||
| Europe | |||||
| Resin Identification | LCP-(MD30+S) | ISO 1043 | |||