- 密度 [g/cm3]: 1.64
- 彎曲模量 [MPa]: 7.10
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.64 g/cc | 0.0592 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.00 cm/cm @Thickness 2.00 mm | 0.00 in/in @Thickness 0.0787 in | Parallel; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0065 cm/cm @Thickness 2.00 mm | 0.0065 in/in @Thickness 0.0787 in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527 | ||
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 | ||
| Tensile Modulus | 10.0 GPa | 1450 ksi | ISO 527 | ||
| Flexural Strength | 145 MPa @Temperature 23.0 °C | 21000 psi @Temperature 73.4 °F | ISO 178 | ||
| Flexural Modulus | 7.10 GPa @Temperature 23.0 °C | 1030 ksi @Temperature 73.4 °F | ISO 178 | ||
| Charpy Impact, Notched | 0.900 J/cm2 @Temperature 23.0 °C | 4.28 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 335 °C | 635 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 355 °C | 671 °F | Optimum | ||
| 350 - 360 °C | 662 - 680 °F | ||||
| Mold Temperature | 80.0 °C | 176 °F | Optimum | ||
| 40.0 - 150 °C | 104 - 302 °F | ||||
| Drying Temperature | 150 °C | 302 °F | |||
| Dry Time | 3 hour | 3 hour | Dehumidified Dryer | ||
| Moisture Content | <= 0.010 % | <= 0.010 % | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Drying Recommended | Yes | ||||
| Forms | Pellets | ||||
| Generic | LCP | ||||
| Part Marking Code | >LCP-MD30< | ISO 11469 | |||
| Product Category | Food Contact Resins | ||||
| Mineral Reinforced Resins | |||||
| Region Available | Americas | ||||
| Asia/Pacific | |||||
| Europe | |||||
| Resin Identification | LCP-MD30 | ISO 1043 | |||