- 缺口沖擊強度: 1.18
- 彎曲模量 [MPa]: 12.753
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.62 g/cc | 1.62 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 132.435 MPa | 19208.1 psi | ASTM D638 |
| Elongation at Break | 1.8 % | 1.8 % | ASTM D638 |
| Flexural Strength | 171.68 MPa | 24900 psi | ASTM D790 |
| Flexural Modulus | 12.753 GPa | 1849.7 ksi | ASTM D790 |
| Izod Impact, Notched | 1.18 J/cm | 2.20 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ASTM D257 |
| Dielectric Constant | 3.9 @Frequency 1.00e+6 Hz | 3.9 @Frequency 1.00e+6 Hz | ASTM D150 |
| Dielectric Strength | 29.0 kV/mm @Thickness 1.60 mm | 737 kV/in @Thickness 0.0630 in | ASTM D149 |
| Dissipation Factor | 0.027 @Frequency 1.00e+6 Hz | 0.027 @Frequency 1.00e+6 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 335 °C | 635 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 350 - 360 °C | 662 - 680 °F | |
| Mold Temperature | 30.0 - 160 °C | 86.0 - 320 °F | |