- 吸水率 [%]: 0.02
- 缺口沖擊強度: 0.0686
- 彎曲模量 [MPa]: 13.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.73 g/cc | 1.73 g/cc | ASTM D792 |
| Water Absorption | 0.020 % @Time 86400 sec | 0.020 % @Time 24.0 hour | |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm | 0.0040 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 111.834 MPa | 16220.2 psi | ASTM D638 |
| Elongation at Break | 1.5 % | 1.5 % | ASTM D638 |
| Flexural Strength | 163.83 MPa | 23762 psi | ASTM D790 |
| Flexural Modulus | 13.2 GPa | 1910 ksi | ASTM D790 |
| Izod Impact, Notched | 0.0686 J/cm | 0.129 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ASTM D257 |
| Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz | 3.6 @Frequency 1.00e+6 Hz | ASTM D150 |
| Dissipation Factor | 0.023 @Frequency 1.00e+6 Hz | 0.023 @Frequency 1.00e+6 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 335 °C | 635 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 269 °C | 516 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 350 - 360 °C | 662 - 680 °F | |
| Mold Temperature | 40.0 - 150 °C | 104 - 302 °F | |