- 密度 [g/cm3]: 1.85
- 彎曲強度 [MPa]: 76.0
- 彎曲模量 [MPa]: 12.5
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.85 g/cc | 0.0668 lb/in3 | ISO 1183 | ||
| Filler Content | 50 % | 50 % | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 88.0 MPa | 12800 psi | ISO 527 | ||
| Tensile Strength, Ultimate | 76.0 MPa @Temperature 23.0 °C | 11000 psi @Temperature 73.4 °F | ASTM D 638 | ||
| Elongation at Break | 1.4 % | 1.4 % | ISO 527 | ||
| 1.2 % @Temperature 23.0 °C | 1.2 % @Temperature 73.4 °F | ASTM D 638 | |||
| Tensile Modulus | 15.8 GPa | 2290 ksi | ISO 527 | ||
| Flexural Strength | 136 MPa | 19700 psi | ASTM D 790 | ||
| 165 MPa | 23900 psi | ISO 178 | |||
| Flexural Modulus | 12.5 GPa @Temperature 23.0 °C | 1810 ksi @Temperature 73.4 °F | ISO 178 | ||
| 15.4 GPa @Temperature 23.0 °C | 2230 ksi @Temperature 73.4 °F | ASTM D 790 | |||
| Charpy Impact, Notched | 0.360 J/cm2 @Temperature 23.0 °C | 1.71 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 | ||
| 175 - 249 V | 175 - 249 V | UL 746A | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 13.0 μm/m-°C @Thickness 4.00 mm, Temperature -40.0 - 23.0 °C | 7.22 μin/in-°F @Thickness 0.157 in, Temperature -40.0 - 73.4 °F | ISO 11359-1/-2 | ||
| 15.0 μm/m-°C @Thickness 4.00 mm, Temperature 23.0 - 55.0 °C | 8.33 μin/in-°F @Thickness 0.157 in, Temperature 73.4 - 131 °F | ISO 11359-1/-2 | |||
| 19.0 μm/m-°C @Thickness 4.00 mm, Temperature 160 - 250 °C | 10.6 μin/in-°F @Thickness 0.157 in, Temperature 320 - 482 °F | ISO 11359-1/-2 | |||
| 20.0 μm/m-°C @Thickness 4.00 mm, Temperature 55.0 - 160 °C | 11.1 μin/in-°F @Thickness 0.157 in, Temperature 131 - 320 °F | ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 25.0 μm/m-°C @Temperature -40.0 - 23.0 °C | 13.9 μin/in-°F @Temperature -40.0 - 73.4 °F | ISO 11359-1/-2; 4mm | ||
| 27.0 μm/m-°C @Thickness 4.00 mm, Temperature 23.0 - 55.0 °C | 15.0 μin/in-°F @Thickness 0.157 in, Temperature 73.4 - 131 °F | ISO 11359-1/-2 | |||
| 34.0 μm/m-°C @Thickness 4.00 mm, Temperature 55.0 - 160 °C | 18.9 μin/in-°F @Thickness 0.157 in, Temperature 131 - 320 °F | ISO 11359-1/-2 | |||
| 37.0 μm/m-°C @Thickness 4.00 mm, Temperature 160 - 250 °C | 20.6 μin/in-°F @Thickness 0.157 in, Temperature 320 - 482 °F | ISO 11359-1/-2 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 278 °C | 532 °F | ASTM D 648 | ||
| 290 °C | 554 °F | ISO 75-1/-2 1993/N2 | |||
| UL RTI, Electrical | 130 °C @Thickness 0.800 mm | 266 °F @Thickness 0.0315 in | UL 746B | ||
| UL RTI, Mechanical with Impact | 130 °C @Thickness 0.800 mm | 266 °F @Thickness 0.0315 in | UL 746B | ||
| UL RTI, Mechanical without Impact | 130 °C @Thickness 0.800 mm | 266 °F @Thickness 0.0315 in | UL 746B | ||
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | IEC 60695-11-10 | ||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | IEC 60695-11-10 | |||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | UL94 | |||
| V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | UL94 | |||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | IEC 60695-11-10 | |||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 335 °C | 635 °F | Optimum | ||
| 330 - 350 °C | 626 - 662 °F | ||||
| Mold Temperature | 80.0 °C | 176 °F | Optimum | ||
| 40.0 - 150 °C | 104 - 302 °F | ||||
| Drying Temperature | 150 °C | 302 °F | |||
| Dry Time | 3 hour | 3 hour | Dehumidified Dryer | ||
| Moisture Content | <= 0.010 % | <= 0.010 % | |||
| Descriptive Properties | |||||
| Color | Black | ||||
| Drying Recommended | Yes | ||||
| Filler | Glass/Mineral | ||||
| Forms | Pellets | ||||
| Generic | LCP | ||||
| Part Marking Code | >LCP-(GF+MD)50< | ISO 11469 | |||
| Polymer Family | LCP | ||||
| Polymer Type | LCP | ||||
| Processing Method | Injection Molding | ||||
| Product Category | Electrical Resins | ||||
| Flame Retardant Resins | |||||
| Glass/Mineral Reinforced Resins | |||||
| Low Warp Resins | |||||
| Region Available | Americas | ||||
| Asia/Pacific | |||||
| Europe | |||||
| Resin Identification | LCP-(GF+MD)50 | ISO 1043 | |||