- 熔體流動速率 [g/10min]: 7.0
- 密度 [g/cm3]: 1.06
- 拉伸強度 [MPa]: 86.0
- 彎曲模量 [MPa]: 4.40
- 熱變形溫度 [℃]: 160.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in3 | ISO 1183 | ||
| Melt Flow | 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 7.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| 34 g/10 min @Load 5.00 kg, Temperature 230 °C | 34 g/10 min @Load 11.0 lb, Temperature 446 °F | ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 124 MPa | 18000 psi | H 385/30; ISO 2039 | ||
| Tensile Strength, Yield | 86.0 MPa | 12500 psi | At 50 mm/min; ISO 527-2 | ||
| Elongation at Yield | 3.0 % | 3.0 % | At 50 mm/min; ISO 527-2 | ||
| Flexural Modulus | 4.40 GPa | 638 ksi | At 2 mm/min; ISO 178 | ||
| Charpy Impact Unnotched | 4.10 J/cm2 | 19.5 ft-lb/in2 | ISO 179/1eU | ||
| 2.50 J/cm2 @Temperature -20.0 °C | 11.9 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.700 J/cm2 | 3.33 ft-lb/in2 | ISO 179/1eA | ||
| 0.570 J/cm2 @Temperature -20.0 °C | 2.71 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | ISO 75-2 | ||
| Vicat Softening Point | 132 °C | 270 °F | B (50N); ISO 306 | ||
| 165 °C | 329 °F | A (10N); ISO 306 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 210 - 260 °C | 410 - 500 °F | |||
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |||
| Descriptive Properties | |||||
| Fogging, mg | 2.3 | At 100°C/ 16 hours | |||