- 熔體流動速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.9
- 拉伸強度 [MPa]: 28.0
- 彎曲模量 [MPa]: 1.30
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in3 | ISO 1183 |
| Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 230 °C | 0.30 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | 50mm/min; ISO 527-2 |
| Elongation at Yield | 6.0 % | 6.0 % | 50mm/min; ISO 527-2 |
| Flexural Modulus | 1.30 GPa | 189 ksi | 2mm/min; ISO 178 |
| Charpy Impact, Notched | 0.450 J/cm2 @Temperature -20.0 °C | 2.14 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA |
| 5.00 J/cm2 @Temperature 23.0 °C | 23.8 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 163 °C | 325 °F | DSC; ISO 3146 |
| Vicat Softening Point | 147 °C @Load 1.02 kg | 297 °F @Load 2.25 lb | ISO 306 |
| Processing Properties | Metric | English | Comments |
| Shelf Life | 18.0 Month | 18.0 Month | |