- 熔體流動(dòng)速率 [g/10min]: 4.0
- 密度 [g/cm3]: 0.904
- 拉伸強(qiáng)度 [MPa]: 22.5
- 硬度: 80.0
- 熱變形溫度 [℃]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.904 g/cc | 0.0327 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage | 0.010 - 0.020 cm/cm | 0.010 - 0.020 in/in | |||
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 4.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 80 | 80 | ISO 2039-2 | ||
| Tensile Strength, Yield | 22.5 MPa | 3260 psi | 50mm/min; ISO 527-2 | ||
| Elongation at Yield | 5.5 % | 5.5 % | 50mm/min; ISO 527-2 | ||
| Tensile Modulus | 1.20 GPa | 174 ksi | 1mm/min; ISO 527-2 | ||
| Charpy Impact, Notched | 0.750 J/cm2 @Temperature -20.0 °C | 3.57 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | ||
| 2.00 J/cm2 @Temperature 23.0 °C | 9.52 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Puncture Energy | 41.0 J @Temperature -40.0 °C | 30.2 ft-lb @Temperature -40.0 °F | ISO 6603-2 | ||
| 46.0 J @Temperature -20.0 °C | 33.9 ft-lb @Temperature -4.00 °F | ISO 6603-2 | |||
| 48.0 J @Temperature 0.000 °C | 35.4 ft-lb @Temperature 32.0 °F | ISO 6603-2 | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | ISO 75-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 230 - 260 °C | 446 - 500 °F | |||
| Mold Temperature | 10.0 - 30.0 °C | 50.0 - 86.0 °F | |||
| Hold Pressure | 20.0 - 50.0 MPa | 2900 - 7250 psi | |||
| Descriptive Properties | |||||
| Injection Velocity | highest possible | ||||