- 熔體流動速率 [g/10min]: 1.8
- 密度 [g/cm3]: 1.18
- 拉伸強度 [MPa]: 115.0
- 彎曲模量 [MPa]: 7.50
- 熱變形溫度 [℃]: 152.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in3 | ISO 1183 |
| Melt Flow | 1.8 g/10 min @Load 2.16 kg, Temperature 230 °C | 1.8 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Spiral Flow | 106 cm @Thickness 2.00 mm, Temperature 250 °C | 41.7 in @Thickness 0.0787 in, Temperature 482 °F | Borealis Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 115 MPa | 16700 psi | ISO 527-2 |
| 48.0 MPa @Temperature 100 °C | 6960 psi @Temperature 212 °F | ISO 527-2 | |
| Elongation at Break | 3.2 % | 3.2 % | ISO 527-2 |
| 5.5 % @Temperature 100 °C | 5.5 % @Temperature 212 °F | ISO 527-2 | |
| Tensile Modulus | 9.00 GPa | 1310 ksi | ISO 527-2 |
| 4.50 GPa @Temperature 100 °C | 653 ksi @Temperature 212 °F | ISO 527-2 | |
| Flexural Strength | 160 MPa | 23200 psi | ISO 178 |
| Flexural Modulus | 7.50 GPa | 1090 ksi | ISO 178 |
| Charpy Impact Unnotched | 5.80 J/cm2 | 27.6 ft-lb/in2 | ISO 179/1eU |
| 5.40 J/cm2 @Temperature -20.0 °C | 25.7 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 1.20 J/cm2 | 5.71 ft-lb/in2 | ISO 179/1eA |
| Impact Test | 9.00 J @Thickness 3.00 mm | 6.64 ft-lb @Thickness 0.118 in | Biaxial, Total Energy; ISO 6603T |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | HDT-A; ISO 75-2 |
| Vicat Softening Point | 140 °C | 284 °F | B (50 N); ISO 306 |
| Shrinkage | 0.80 - 1.2 % | 0.80 - 1.2 % | Cross Flow Direction; Borealis Method |
| 0.20 - 0.30 % @Thickness 4.00 mm | 0.20 - 0.30 % @Thickness 0.157 in | In Flow Direction; Borealis Method | |
| <= 0.30 % @Thickness 4.00 mm | <= 0.30 % @Thickness 0.157 in | In Flow Direction; Borealis Method | |
| Optical Properties | Metric | English | Comments |
| Gloss | 82 % @Thickness 2.00 mm | 82 % @Thickness 0.0787 in | 20°, plaque; DIN 67530 |
| 90 % @Thickness 2.00 mm | 90 % @Thickness 0.0787 in | 60°, 2 mm plaque; DIN 67530 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 230 - 260 °C | 446 - 500 °F | |
| Mold Temperature | 50.0 - 60.0 °C | 122 - 140 °F | |