- 熔體流動速率 [g/10min]: 6.0
- 密度 [g/cm3]: 1.01
- 拉伸強度 [MPa]: 20.0
- 彎曲模量 [MPa]: 1.60
- 熱變形溫度 [℃]: 91.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | Borealis Method | ||
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 6.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| 30 g/10 min @Load 5.00 kg, Temperature 230 °C | 30 g/10 min @Load 11.0 lb, Temperature 446 °F | ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 50.0 MPa | 7250 psi | H385/30; ISO 2039 | ||
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | At 50 mm/min; ISO 527-2 | ||
| Elongation at Yield | 5.3 % | 5.3 % | At 50 mm/min; ISO 527-2 | ||
| Flexural Modulus | 1.60 GPa | 232 ksi | At 2 mm/min; ISO 178 | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| 5.10 J/cm2 @Temperature -20.0 °C | 24.3 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 2.50 J/cm2 | 11.9 ft-lb/in2 | ISO 179/1eA | ||
| 0.430 J/cm2 @Temperature -20.0 °C | 2.05 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-2 | ||
| Vicat Softening Point | 51.0 °C | 124 °F | B (50N); ISO 306 | ||
| 128 °C | 262 °F | A (10N); ISO 306 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 210 - 260 °C | 410 - 500 °F | |||
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |||
| Descriptive Properties | |||||
| Emissions, ug C/g | 45 | VDA 277 | |||
| Fogging % | 96.4 | At 100°C/3 hours | |||
| Fogging, mg | 0.5 | At 100°C/ 16 hours | |||