- 熔體流動速率 [g/10min]: 20.0
- 密度 [g/cm3]: 1.12
- 拉伸強度 [MPa]: 16.0
- 彎曲模量 [MPa]: 2.20
- 熱變形溫度 [℃]: 95.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | Borealis Method |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 230 °C | 20 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 16.0 MPa | 2320 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Break | 123 % | 123 % | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 4.0 % | 4.0 % | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 2.10 GPa | 305 ksi | At 1 mm/min; ISO 527-2 |
| Flexural Strength | 23.5 MPa | 3410 psi | ISO 178 |
| Flexural Modulus | 2.20 GPa | 319 ksi | At 2 mm/min; ISO 178 |
| Charpy Impact Unnotched | 4.50 J/cm2 | 21.4 ft-lb/in2 | ISO 179/1eU |
| 4.50 J/cm2 @Temperature -20.0 °C | 21.4 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 1.30 J/cm2 | 6.19 ft-lb/in2 | ISO 179/1eA |
| 0.200 J/cm2 @Temperature -30.0 °C | 0.952 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | |
| 0.350 J/cm2 @Temperature -20.0 °C | 1.67 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 19.0 μm/m-°C @Temperature -30.0 - 80.0 °C | 10.6 μin/in-°F @Temperature -22.0 - 176 °F | Borealis Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C | 203 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 51.0 °C | 124 °F | ISO 75-2 |
| Vicat Softening Point | 36.0 °C | 96.8 °F | B (50N); ISO 306 |
| Shrinkage | 0.10 % | 0.10 % | Borealis Method |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | Polymer Mass Temp |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |