- 熔體流動速率 [g/10min]: 6.0
- 密度 [g/cm3]: 1.04
- 拉伸強度 [MPa]: 32.0
- 彎曲模量 [MPa]: 2.80
- 熱變形溫度 [℃]: 121.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0090 cm/cm | 0.0090 in/in | 150x80x20 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | 150x80x20; Borealis Method |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 6.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| 26 g/10 min @Load 5.00 kg, Temperature 230 °C | 26 g/10 min @Load 11.0 lb, Temperature 446 °F | ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 82.0 MPa | 11900 psi | H385/30; ISO 2039 |
| Tensile Strength, Yield | 32.00 MPa | 4641 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 4.9 % | 4.9 % | At 50 mm/min; ISO 527-2 |
| Flexural Modulus | 2.80 GPa | 406 ksi | At 5 mm/min; ISO 178 |
| Charpy Impact Unnotched | 4.30 J/cm2 | 20.5 ft-lb/in2 | ISO 179/1eU |
| 1.40 J/cm2 @Temperature -20.0 °C | 6.66 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.230 J/cm2 | 1.09 ft-lb/in2 | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 121 °C | 250 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75-2 |
| Vicat Softening Point | 89.0 °C | 192 °F | B (50N); ISO 306 |
| 154 °C | 309 °F | A (10N); ISO 306 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 210 - 260 °C | 410 - 500 °F | Polymer Mass Temp |
| Mold Temperature | 30.0 - 60.0 °C | 86.0 - 140 °F | |