- 熔體流動速率 [g/10min]: 2.0
- 密度 [g/cm3]: 1.12
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | Borealis Method |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Elongation at Break | 2.1 % | 2.1 % | ISO 527-2 |
| Tensile Modulus | 7.40 GPa | 1070 ksi | At 1 mm/min; ISO 527-2 |
| Charpy Impact Unnotched | 4.70 J/cm2 | 22.4 ft-lb/in2 | ISO 179/1eU |
| 4.10 J/cm2 @Temperature -20.0 °C | 19.5 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 2.30 J/cm2 | 10.9 ft-lb/in2 | ISO 179/1eA |
| 2.60 J/cm2 @Temperature -20.0 °C | 12.4 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | ISO 75-2 |
| Vicat Softening Point | 145 °C | 293 °F | B (50N); ISO 306 |
| Shrinkage | 1.7 % | 1.7 % | Post Shrinkage at 90°C for 2 hrs.; Borealis Method |
| Processing Properties | Metric | English | Comments |
| Front Barrel Temperature | 220 - 240 °C | 428 - 464 °F | |
| Melt Temperature | 240 - 270 °C | 464 - 518 °F | |
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |
| Screw Speed | 30 - 150 rpm | 30 - 150 rpm | |