- 熔體流動速率 [g/10min]: 2.0
- 密度 [g/cm3]: 1.24
- 彎曲模量 [MPa]: 8.40
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | Borealis Method | ||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Elongation at Break | 2.0 % | 2.0 % | ISO 527-2 | ||
| Tensile Modulus | 9.00 GPa | 1310 ksi | At 1 mm/min; ISO 527-2 | ||
| Flexural Modulus | 8.40 GPa | 1220 ksi | At 2 mm/min; ISO 178 | ||
| Charpy Impact Unnotched | 5.70 J/cm2 | 27.1 ft-lb/in2 | ISO 179/1eU | ||
| 5.50 J/cm2 @Temperature -20.0 °C | 26.2 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 2.80 J/cm2 | 13.3 ft-lb/in2 | ISO 179/1eA | ||
| 3.20 J/cm2 @Temperature -20.0 °C | 15.2 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 162 °C | 324 °F | ISO 75-2 | ||
| Vicat Softening Point | 145 °C | 293 °F | B (50N); ISO 306 | ||
| Processing Properties | Metric | English | Comments | ||
| Front Barrel Temperature | 220 - 240 °C | 428 - 464 °F | |||
| Melt Temperature | 240 - 270 °C | 464 - 518 °F | |||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |||
| Screw Speed | 30 - 150 rpm | 30 - 150 rpm | |||
| Descriptive Properties | |||||
| Fogging, mg | 1.7 | At 100°C/ 16 hours | |||