- 熔體流動(dòng)速率 [g/10min]: 0.85
- 密度 [g/cm3]: 0.9
- 彎曲模量 [MPa]: 1.20
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 - 0.910 g/cc | 0.0325 - 0.0329 lb/in3 | ISO 1183 |
| Melt Flow | 0.85 g/10 min @Load 2.16 kg, Temperature 230 °C | 0.85 g/10 min @Load 4.76 lb, Temperature 446 °F | 50% relative humidity; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 550 - 750 % | 550 - 750 % | ISO 527-3 |
| Film Elongation at Break, TD | 550 - 750 % | 550 - 750 % | ISO 527-3 |
| Tensile Modulus | 0.500 - 0.600 GPa | 72.5 - 87.0 ksi | MD/TD; ISO 527-3 |
| Flexural Modulus | 1.20 GPa | 174 ksi | ISO 178 |
| Dart Drop, Total Energy | 25.0 J @Thickness 0.0500 mm | 18.4 ft-lb @Thickness 0.00197 in | 1100 N force; ISO 7765-2 |
| Film Tensile Strength at Break, MD | 40.0 - 60.0 MPa | 5800 - 8700 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 30.0 - 50.0 MPa | 4350 - 7250 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 158 - 162 °C | 316 - 324 °F | 50% humidity, 23°C; ISO 3146 |
| Vicat Softening Point | 150 °C @Load 1.02 kg | 302 °F @Load 2.25 lb | 50% humidity, 23°C; ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | <= 40 % | <= 40 % | ASTM D1003 |
| Gloss | >= 3.0 % | >= 3.0 % | ASTM D2457 |