- 熔體流動速率 [g/10min]: 4.0
- 密度 [g/cm3]: 1.15
- 拉伸強(qiáng)度 [MPa]: 108.0
- 彎曲強(qiáng)度 [MPa]: 45.0
- 彎曲模量 [MPa]: 6.80
- 熱變形溫度 [℃]: 152.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in3 | ISO 1183 |
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 4.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Spiral Flow | 95.0 cm @Thickness 2.00 mm, Temperature 250 °C | 37.4 in @Thickness 0.0787 in, Temperature 482 °F | Borealis Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 45.0 MPa @Temperature 100 °C | 6530 psi @Temperature 212 °F | ISO 527-2 |
| Tensile Strength, Yield | 108 MPa | 15700 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Break | 2.9 % | 2.9 % | ISO 527-2 |
| 7.5 % @Temperature 100 °C | 7.5 % @Temperature 212 °F | ISO 527-2 | |
| Elongation at Yield | 3.2 % | 3.2 % | Flexural Strain; ISO 178 |
| Tensile Modulus | 8.10 GPa | 1170 ksi | ISO 527-2 |
| 3.50 GPa @Temperature 100 °C | 508 ksi @Temperature 212 °F | ISO 527-2 | |
| Flexural Strength | 145 MPa | 21000 psi | ISO 178 |
| Flexural Modulus | 6.80 GPa | 986 ksi | ISO 178 |
| Charpy Impact Unnotched | 4.70 J/cm2 | 22.4 ft-lb/in2 | ISO 179/1eU |
| 4.40 J/cm2 @Temperature -20.0 °C | 20.9 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.950 J/cm2 | 4.52 ft-lb/in2 | ISO 179/1eA |
| 0.850 J/cm2 @Temperature -20.0 °C | 4.05 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | |
| Impact Test | 5.00 J | 3.69 ft-lb | At -20°C; ISO 6603T |
| 6.50 J @Thickness 3.00 mm | 4.79 ft-lb @Thickness 0.118 in | Biaxial, Total Energy; ISO 6603T | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | HDT-A; ISO 75-2 |
| Vicat Softening Point | 138 °C | 280 °F | B (50 N); ISO 306 |
| Shrinkage | >= 1.0 % | >= 1.0 % | Cross Flow Direction; Borealis Method |
| <= 1.55 % | <= 1.55 % | Testbox; Borealis Method | |
| <= 0.20 % @Thickness 2.00 mm | <= 0.20 % @Thickness 0.0787 in | In Flow Direction; Borealis Method | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 220 - 270 °C | 428 - 518 °F | |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |