- 熔體流動(dòng)速率 [g/10min]: 15.0
- 密度 [g/cm3]: 0.905
- 拉伸強(qiáng)度 [MPa]: 20.99
- 硬度: 70.0
- 熱變形溫度 [℃]: 75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 230 °C | 15 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 70 | 70 | ISO 2039-2 |
| Tensile Strength, Yield | 20.99 MPa | 3045 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 7.0 % | 7.0 % | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 1.00 GPa | 145 ksi | At 1 mm/min; ISO 527-2 |
| Charpy Impact, Notched | 1.40 J/cm2 | 6.66 ft-lb/in2 | ISO 179/1eA |
| 0.600 J/cm2 @Temperature -20.0 °C | 2.86 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | |
| Impact Test | 36.0 J | 26.6 ft-lb | Total Penetration Energy at 0°C; ISO 6603-2 |
| 39.0 J | 28.8 ft-lb | Total Penetration Energy at -20°C; ISO 6603-2 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 75.0 °C | 167 °F | ISO 75-2 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 210 - 260 °C | 410 - 500 °F | |
| Mold Temperature | 30.0 - 40.0 °C | 86.0 - 104 °F | |