- 熔體流動(dòng)速率 [g/10min]: 25.0
- 密度 [g/cm3]: 0.9
- 拉伸強(qiáng)度 [MPa]: 17.0
- 熱變形溫度 [℃]: 59.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage | 0.010 - 0.020 cm/cm | 0.010 - 0.020 in/in | |
| Melt Flow | 25 g/10 min @Load 2.16 kg, Temperature 230 °C | 25 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 50 | 50 | ISO 868 |
| Tensile Strength, Yield | 17.00 MPa | 2465 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 15 % | 15 % | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 0.600 GPa | 87.0 ksi | At 1 mm/min; ISO 527-2 |
| Charpy Impact, Notched | 2.00 J/cm2 | 9.52 ft-lb/in2 | ISO 179/1eA |
| 0.650 J/cm2 @Temperature -20.0 °C | 3.09 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | |
| Impact Test | 18.0 J | 13.3 ft-lb | Total Penetration Energy; ISO 6603-2 |
| 30.0 J | 22.1 ft-lb | Total Penetration Energy at -20°C; ISO 6603-2 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 59.0 °C | 138 °F | ISO 75-2 |
| Vicat Softening Point | 45.0 °C | 113 °F | 50 N; ISO 306 |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 210 - 250 °C | 410 - 482 °F | |
| Mold Temperature | 30.0 - 60.0 °C | 86.0 - 140 °F | |