- 熔體流動速率 [g/10min]: 13.0
- 密度 [g/cm3]: 0.905
- 拉伸強度 [MPa]: 22.99
- 硬度: 67.0
- 熱變形溫度 [℃]: 72.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage | 0.010 - 0.020 cm/cm | 0.010 - 0.020 in/in | |
| Melt Flow | 13 g/10 min @Load 2.16 kg, Temperature 230 °C | 13 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 67 | 67 | ISO 2039-2 |
| Tensile Strength, Yield | 22.99 MPa | 3335 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 14 % | 14 % | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 0.900 GPa | 131 ksi | At 1 mm/min; ISO 527-2 |
| Charpy Impact, Notched | 0.800 J/cm2 | 3.81 ft-lb/in2 | ISO 179/1eA |
| 0.200 J/cm2 @Temperature -20.0 °C | 0.952 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | |
| 0.400 J/cm2 @Temperature 0.000 °C | 1.90 ft-lb/in2 @Temperature 32.0 °F | ISO 179/1eA | |
| Impact Test | 5.00 J | 3.69 ft-lb | Total Penetration Energy at -10°C; ISO 6603-2 |
| 20.0 J | 14.8 ft-lb | Total Penetration Energy at 0°C; ISO 6603-2 | |
| 35.0 J | 25.8 ft-lb | Total Penetration Energy; ISO 6603-2 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ISO 75-2 |
| Optical Properties | Metric | English | Comments |
| Haze | 21 % @Thickness 1.00 mm | 21 % @Thickness 0.0394 in | plaque; Borealis Method |
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | |
| Mold Temperature | 20.0 - 60.0 °C | 68.0 - 140 °F | |