- 熔體流動速率 [g/10min]: 12.0
- 密度 [g/cm3]: 0.91
- 拉伸強度 [MPa]: 19.5
- 彎曲模量 [MPa]: 1.05
- 熱變形溫度 [℃]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | Borealis Method |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C | 12 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 19.50 MPa | 2828 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Break | 570 % | 570 % | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 9.0 % | 9.0 % | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 1.05 GPa | 152 ksi | At 1 mm/min; ISO 527-2 |
| Flexural Strength | 22.0 MPa | 3190 psi | ISO 178 |
| Flexural Modulus | 1.05 GPa | 152 ksi | At 2 mm/min; ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| NB @Temperature -20.0 °C | NB @Temperature -4.00 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 4.20 J/cm2 | 20.0 ft-lb/in2 | ISO 179/1eA |
| 0.500 J/cm2 @Temperature -30.0 °C | 2.38 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | |
| 0.700 J/cm2 @Temperature -20.0 °C | 3.33 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 49.0 °C | 120 °F | ISO 75-2 |
| Vicat Softening Point | 63.0 °C | 145 °F | B (50N); ISO 306 |
| 130 °C | 266 °F | A (10N); ISO 306 | |
| Shrinkage | 0.15 % | 0.15 % | Post Shrinkage at 90°C for 2 hrs.; Borealis Method |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | Polymer Mass Temp |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |