- 熔體流動速率 [g/10min]: 6.5
- 密度 [g/cm3]: 1.02
- 缺口沖擊強度: 35.0
- 拉伸強度 [MPa]: 16.0
- 彎曲模量 [MPa]: 1.70
- 熱變形溫度 [℃]: 98.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | Borealis Method |
| Melt Flow | 6.5 g/10 min @Load 2.16 kg, Temperature 230 °C | 6.5 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 16.0 MPa | 2320 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Break | 80 % | 80 % | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 4.7 % | 4.7 % | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 1.50 GPa | 218 ksi | At 1 mm/min; ISO 527-2 |
| Flexural Strength | 24.5 MPa | 3550 psi | ISO 178 |
| Flexural Modulus | 1.70 GPa | 247 ksi | At 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 35.0 kJ/m2 | 16.7 ft-lb/in2 | ISO 180/1A |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| NB @Temperature -20.0 °C | NB @Temperature -4.00 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 4.00 J/cm2 | 19.0 ft-lb/in2 | ISO 179/1eA |
| 0.400 J/cm2 @Temperature -30.0 °C | 1.90 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | |
| 1.00 J/cm2 @Temperature -20.0 °C | 4.76 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 43.0 °C | 109 °F | ISO 75-2 |
| Vicat Softening Point | 39.0 °C | 102 °F | B (50N); ISO 306 |
| 118 °C | 244 °F | A (10N); ISO 306 | |
| Shrinkage | 0.10 % | 0.10 % | Post Shrinkage at 90°C for 2 hrs.; Borealis Method |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |