- 熔體流動(dòng)速率 [g/10min]: 8.0
- 密度 [g/cm3]: 0.9
- 彎曲模量 [MPa]: 2.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 - 0.910 g/cc | 0.0325 - 0.0329 lb/in3 | ISO 1183 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 8.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 80 % | 80 % | ISO 527-3 |
| Film Elongation at Break, TD | 120 % | 120 % | ISO 527-3 |
| Flexural Modulus | 2.10 GPa | 305 ksi | ISO 178 |
| Secant Modulus, MD | 1.60 GPa | 232 ksi | ISO 527-3 |
| Secant Modulus, TD | 1.80 GPa | 261 ksi | ISO 527-3 |
| Impact | 40 | 40 | Dynatest, Damaging Force (N); ISO 7765-2 |
| Impact Test | 0.950 J | 0.701 ft-lb | Dynatest, Penetration Energy; ISO 7765-2 |
| Coefficient of Friction | 0.30 - 0.40 | 0.30 - 0.40 | Film/Film; ISO 8295 |
| Film Tensile Strength at Break, MD | 35.0 - 55.0 MPa | 5080 - 7980 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 30.0 - 50.0 MPa | 4350 - 7250 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 164 - 170 °C | 327 - 338 °F | ISO 3146 |
| Vicat Softening Point | 158 °C | 316 °F | A (10 N); ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | <= 6.0 % | <= 6.0 % | ASTM D1003 |
| Gloss | >= 90 % | >= 90 % | ASTM D2457 |