- 熔體流動速率 [g/10min]: 20.0
- 密度 [g/cm3]: 0.905
- 拉伸強度 [MPa]: 27.0
- 硬度: 89.0
- 熱變形溫度 [℃]: 105.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage | 0.015 - 0.020 cm/cm | 0.015 - 0.020 in/in | |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 230 °C | 20 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 89 | 89 | ISO 2039-2 |
| Tensile Strength, Yield | 27.00 MPa | 3916 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 5.0 % | 5.0 % | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 1.50 GPa | 218 ksi | At 1 mm/min; ISO 527-2 |
| Charpy Impact, Notched | 0.850 J/cm2 | 4.05 ft-lb/in2 | ISO 179/1eA |
| 0.450 J/cm2 @Temperature -20.0 °C | 2.14 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | |
| Impact Test | 15.0 J | 11.1 ft-lb | Total Penetration Energy at -20°C; ISO 6603-2 |
| 20.0 J | 14.8 ft-lb | Total Penetration Energy at 0°C; ISO 6603-2 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ISO 75-2 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 210 - 260 °C | 410 - 500 °F | |
| Mold Temperature | 10.0 - 30.0 °C | 50.0 - 86.0 °F | |