- 熔體流動(dòng)速率 [g/10min]: 20.0
- 密度 [g/cm3]: 0.905
- 拉伸強(qiáng)度 [MPa]: 28.0
- 硬度: 90.0
- 熱變形溫度 [℃]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in3 | ASTM D792 |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 230 °C | 20 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 90 | 90 | ASTM D785 |
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | At 50 mm/min; ASTM D638 |
| Elongation at Yield | 12 % | 12 % | At 50 mm/min; ASTM D638 |
| Tensile Modulus | 1.15 GPa | 167 ksi | At 1 mm/min; ASTM D638 |
| Charpy Impact, Notched | 0.600 J/cm2 | 2.86 ft-lb/in2 | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | ASTM D648 |