- 熔體流動速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.7
- 拉伸強度 [MPa]: 11.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.700 g/cc | 0.0253 lb/in3 | ISO 1183 |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 11.0 MPa | 1600 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Break | >= 50 % | >= 50 % | 50 mm/min; ISO 527-3 |
| Tensile Modulus | 2.00 GPa | 290 ksi | At 1 mm/min; ISO 178 |
| Compressive Strength | 17.0 MPa | 2470 psi | 5% Compression; ASTM D695 |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 0.160 W/m-K | 1.11 BTU-in/hr-ft2-°F | ASTM C 177 |
| Vicat Softening Point | 148 °C | 298 °F | A (10 N); ISO 306 |
| Processing Properties | Metric | English | Comments |
| Front Barrel Temperature | 220 - 240 °C | 428 - 464 °F | |
| Melt Temperature | 225 - 235 °C | 437 - 455 °F | |
| Head Temperature | 220 - 230 °C | 428 - 446 °F | |