- 熔體流動速率 [g/10min]: 1.9
- 密度 [g/cm3]: 0.902
- 拉伸強度 [MPa]: 26.2
- 熱變形溫度 [℃]: 83.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.902 g/cc | 0.0326 lb/in3 | ASTM D792 |
| Melt Flow | 1.9 g/10 min @Load 2.16 kg, Temperature 230 °C | 1.9 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 26.2 MPa | 3800 psi | At 50 mm/min; ASTM D638 |
| Elongation at Yield | 13 % | 13 % | At 50 mm/min; ASTM D638 |
| Tensile Modulus | 1.00 GPa | 145 ksi | At 1 mm/min; ASTM D638 |
| Charpy Impact, Notched | 0.700 J/cm2 | 3.33 ft-lb/in2 | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 83.0 °C | 181 °F | ASTM D648 |