- 熔體流動速率 [g/10min]: 30.0
- 密度 [g/cm3]: 0.905
- 拉伸強度 [MPa]: 27.5
- 硬度: 90.0
- 熱變形溫度 [℃]: 82.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in3 | ISO 1183 |
| Melt Flow | 30 g/10 min @Load 2.16 kg, Temperature 230 °C | 30 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 90 | 90 | ISO 2039-2 |
| Tensile Strength, Yield | 27.50 MPa | 3988 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 12 % | 12 % | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 1.20 GPa | 174 ksi | At 1 mm/min; ISO 527-2 |
| Charpy Impact, Notched | 0.600 J/cm2 | 2.86 ft-lb/in2 | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 82.0 °C | 180 °F | ISO 75-2 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 220 - 250 °C | 428 - 482 °F | |
| Mold Temperature | 30.0 - 40.0 °C | 86.0 - 104 °F | |