- 熔體流動速率 [g/10min]: 6.0
- 密度 [g/cm3]: 0.95
- 拉伸強度 [MPa]: 17.0
- 彎曲模量 [MPa]: 1.40
- 熱變形溫度 [℃]: 87.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | Borealis Method | ||
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 6.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| 30 g/10 min @Load 5.00 kg, Temperature 230 °C | 30 g/10 min @Load 11.0 lb, Temperature 446 °F | ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 33.0 MPa | 4790 psi | H385/30; ISO 2039 | ||
| Tensile Strength, Yield | 17.00 MPa | 2465 psi | At 50 mm/min; ISO 527-2 | ||
| Elongation at Yield | 5.5 % | 5.5 % | At 50 mm/min; ISO 527-2 | ||
| Flexural Modulus | 1.40 GPa | 203 ksi | At 2 mm/min; ISO 178 | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| 19.5 J/cm2 @Temperature -20.0 °C | 92.8 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 5.50 J/cm2 | 26.2 ft-lb/in2 | ISO 179/1eA | ||
| 0.600 J/cm2 @Temperature -20.0 °C | 2.86 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 87.0 °C | 189 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 51.0 °C | 124 °F | ISO 75-2 | ||
| Vicat Softening Point | 41.0 °C | 106 °F | B (50N); ISO 306 | ||
| 140 °C | 284 °F | A (10N); ISO 306 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 210 - 260 °C | 410 - 500 °F | |||
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |||
| Descriptive Properties | |||||
| Emissions, ug C/g | 17 | VDA 277 | |||
| Fogging % | 94.5 | At 100°C/3 hours | |||
| Fogging, mg | 1.1 | At 100°C/ 16 hours | |||