- 熔體流動速率 [g/10min]: 2.8
- 密度 [g/cm3]: 0.905
- 拉伸強度 [MPa]: 39.5
- 彎曲模量 [MPa]: 2.00
- 熱變形溫度 [℃]: 118.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage | 0.015 - 0.020 cm/cm | 0.015 - 0.020 in/in | |
| Melt Flow | 2.8 g/10 min @Load 2.16 kg, Temperature 230 °C | 2.8 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 39.50 MPa | 5729 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 7.0 % | 7.0 % | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 2.10 GPa | 305 ksi | At 1 mm/min; ISO 527-2 |
| Flexural Modulus | 2.00 GPa | 290 ksi | At 2 mm/min; ISO 178 |
| Charpy Impact, Notched | 0.400 J/cm2 | 1.90 ft-lb/in2 | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 164 - 168 °C | 327 - 334 °F | ISO 3146 |
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ISO 75-2 |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 210 - 240 °C | 410 - 464 °F | |
| Mold Temperature | 20.0 - 40.0 °C | 68.0 - 104 °F | |