- 熔體流動速率 [g/10min]: 12.0
- 密度 [g/cm3]: 0.95
- 缺口沖擊強度: 35.0
- 拉伸強度 [MPa]: 18.0
- 彎曲模量 [MPa]: 1.50
- 熱變形溫度 [℃]: 92.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | Borealis Method |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C | 12 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Break | 60 % | 60 % | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 5.0 % | 5.0 % | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 1.40 GPa | 203 ksi | At 1 mm/min; ISO 527-2 |
| Flexural Strength | 24.5 MPa | 3550 psi | ISO 178 |
| Flexural Modulus | 1.50 GPa | 218 ksi | At 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 35.0 kJ/m2 | 16.7 ft-lb/in2 | ISO 180/1A |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| NB @Temperature -20.0 °C | NB @Temperature -4.00 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 6.00 J/cm2 | 28.6 ft-lb/in2 | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 67.0 μm/m-°C @Temperature -30.0 - 80.0 °C | 37.2 μin/in-°F @Temperature -22.0 - 176 °F | Borealis Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75-2 |
| Vicat Softening Point | 45.0 °C | 113 °F | B (50N); ISO 306 |
| Shrinkage | 0.15 % | 0.15 % | Post Shrinkage at 90°C for 2 hrs.; Borealis Method |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | Polymer Mass Temp |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |