- 熔體流動速率 [g/10min]: 35.0
- 密度 [g/cm3]: 0.9
- 缺口沖擊強度: 0.534
- 拉伸強度 [MPa]: 26.2
- 彎曲強度 [MPa]: 24.1
- 彎曲模量 [MPa]: 1.17
- 硬度: 78.0
- 熱變形溫度 [℃]: 88.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in3 | ASTM D1505 | ||
| Melt Flow | 35 g/10 min @Load 2.16 kg, Temperature 230 °C | 35 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 78 | 78 | ASTM D785 | ||
| Tensile Strength, Ultimate | 24.1 MPa | 3500 psi | 50 mm/min (2 in./min.); ASTM D638 | ||
| Tensile Strength, Yield | 26.2 MPa | 3800 psi | 50 mm/min (2 in./min.); ASTM D638 | ||
| Elongation at Break | 550 % | 550 % | 50 mm/min (2 in./min.); ASTM D638 | ||
| Elongation at Yield | 11 % | 11 % | 50 mm/min (2 in./min.); ASTM D638 | ||
| Flexural Modulus | 1.17 GPa | 170 ksi | Secant @ 1% strain; ASTM D790 | ||
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ASTM D648 | ||
| Descriptive Properties | |||||
| process | Injection Molding | ||||
| region | Europe/Turkey | ||||